Adsorption of silver ions by hydroxyapatite-alginate microspheres

Abstract

Hydroxyapatite (HA) was chosen as a basic component for biomaterials due to its high sorption capacity to metal ions, biocompatibility, osteoconductivity and thermodynamic stability. Obtained HA-Alg mixture was immersed into 0.1 M AgNO3 solution. Then the concentrations of Ag+ ions in the filtrate were determined by nephelometric analysis. After 60 and 120 min silver was adsorbed only by the surface layer but after prolonged contact it was absorbed completely. More than 60 % of Ag+ ions from solution are incorporated in HA structure. First the silver orthophosphate was formed and then it was destructed under UV-light with following formation of silver nanoparticles.

Гідроксиапатит був обраний як базовий компонент біоматеріалів через його високу сорбційну здатність до іонів металів, біологічну сумісність, остеопровідність та термодинамічну стабільністью. Отримана гідроксиапатит-альгінатна суміш вміщувалася у 0.1 M розчин AgNO3 . Концентрацію іонв Ag+ у фільтраті визначали нефелометричним аналізом . Після 60 та 120 хвилин срібло адсорбувалося лише поверхневим шаром, але після більш тривалого контакту воно адсорбувалося повінстю. Більше 60% іонів срібла з розчину вбудовувалося в структуру гідроксиапатиту. Спочатку утоворювався ортофосфат срібла, який в подальшому розкладався дією ультрафіолету з утворенням наночасточок срібла.