Electric-spark coatings on a steel base and contact surface for optimizing the working characteristics of babbitt friction bearings

Abstract

It is found that the use of transition layers of copper, coated by the electric-spark method in a protective argon atmosphere, improves the heat removal from the contact area and increases the steel bases’ adhesion strength with an antifriction babbitt layer as compared with the traditional technology by 35%. Electric-spark alloying babbitt B83 by indium and stannum allowed us to form running-in coatings without hard inclusions with a thickness of 130 and 100 microns, respectively. New technological solutions allow decreasing the temperature in the friction zone, increasing the thickness of the oil layer, and, as a result, creating a bearing with a better load carrying capability and reliability. Встановлено, що застосування перехідних шарів з міді, що наноситься електроіскровим методом в захисному середовищі аргону, покращує тепловідвід із зони контакту і підвищує міцність з'єднання сталевої підкладки з антифрикційним бабітовим шаром в порівнянні з традиційною технологією на 35%. Електроіскрове легування поверхні бабіту Б83 індієм і оловом дозволило сформувати припрацювальне покриття без твердих включень товщиною відповідно до 130 і 100 мкм. Нові технологічні рішення надали можливість знизити температуру в зоні тертя, підвищити товщину шару мастила і таким чином створити підшипник, що має більшу несучу здатність, надійність.