Magneto-Optical and Magnetic Properties of Three-Layer Films Based on Permalloy and Copper

Abstract

Three-layer nanostructured films FexNi100–x/Cu/FexNi100–x consisting of Fe0,5Ni0,5 alloy layers separated by Cu layer were obtained by layers-by-layers vacuum condensation at the pressure of 10−4 Pa. The magnetic hysteresis loops obtained in the transverse geometry have an almost rectangular shape, which is typical for single-layer films of ferromagnetic metals and alloys based on them and indicates the presence of an axis of easy magnetization in the plane of the sample. Magnetization in the direction perpendicular to the plane of the film shows the action of a strong demagnetizing field. After thermal stabilization of the films, the dependence does not change significantly. Тришарові наноструктуровані плівки FexNi100–x/Cu/FexNi100–x, що складаються з сплавів Fe0,5Ni0,5, розділених шаром Cu, були отримані шарами пошарово вакуумна конденсація при тиску 10–4 Па. Магнітні петлі гістерезису, отримані в поперечній геометрії, мають майже прямокутну форму, що характерно для одношарових плівок феромагнітних металів і сплавів на їх основі і вказує на наявність вісі легкої намагніченості в площині зразка. Намагнічування в напрямку, перпендикулярному площині плівки, показує дію сильного розмагнічуючого поля. Після термічної стабілізації плівок залежність суттєво не змінюється.